FORMAT TAS
Description
MATERIAL FOR RIGID THERMOPLASTIC HANDS
ARTICLE/THICKNESS
FORMAT TAS 10 1.10 ± 0.05 mm
FORMAT TAS 12 1.25 ± 0.05 mm
FORMAT TAS 14 1.45 ± 0.05 mm
FORMAT TAS 16 1.60 ± 0.05 mm
FORMAT TAS 17 1.70 ± 0.05 mm
FORMAT TAS 18 1.80 ± 0.05 mm
FORMAT TAS 20 2.00 ± 0.05 mm
SPECIFICATIONS
FORMAT TAS materials have good mold resistance and good data for hot forming.
It is recommended for numerous types of shoes, both for men (classic, casual, sports, special), and for women.
INSTRUCTIONS FOR USE
The material can be cut in any direction. It is also recommended to soften the backdrop under the infrared lamp before inserting it into the pocket between the lining and the top.
The material should be molded at a temperature of 100-120° C, under a pressure of +/- 5 bar for 10-15 seconds (depending on the thickness of the backdrop and leather goods). Time can be shortened if the equipment is equipped with a heating pad.
Sheet size - 1 m x 1.5 m (sheets on a pallet).
ARTICLE/THICKNESS
FORMAT TAS 10 1.10 ± 0.05 mm
FORMAT TAS 12 1.25 ± 0.05 mm
FORMAT TAS 14 1.45 ± 0.05 mm
FORMAT TAS 16 1.60 ± 0.05 mm
FORMAT TAS 17 1.70 ± 0.05 mm
FORMAT TAS 18 1.80 ± 0.05 mm
FORMAT TAS 20 2.00 ± 0.05 mm
SPECIFICATIONS
- SHEET: 100X150 cm
- ADHESIVE: bilateral
FORMAT TAS materials have good mold resistance and good data for hot forming.
It is recommended for numerous types of shoes, both for men (classic, casual, sports, special), and for women.
INSTRUCTIONS FOR USE
The material can be cut in any direction. It is also recommended to soften the backdrop under the infrared lamp before inserting it into the pocket between the lining and the top.
The material should be molded at a temperature of 100-120° C, under a pressure of +/- 5 bar for 10-15 seconds (depending on the thickness of the backdrop and leather goods). Time can be shortened if the equipment is equipped with a heating pad.
Sheet size - 1 m x 1.5 m (sheets on a pallet).